Keim's process
Keim's process is a technique of fresco preparation and painting intended to maximize the lifetime of the finished work. The process, as reported in 1884 at the Royal Society of Arts in London, was created by chemist and craftsman Adolf Wilhelm Keim of Munich, as an improvement on the earlier "stereochromy" technique of Schlotthaner and Johann Nepomuk von Fuchs.[1][2][3][4]
The process
- First, the surface to be painted is prepared by removing any damp bricks, overly burnt bricks, or decayed wood, and replacing these, and also removing any existing traces of stucco.
- The surface is then coated with a mixture of quartz sand, infusorial earth (calcined fossil meal), and powdered marble, mixed four parts to one with quicklime slaked with distilled water. The purpose of this layer is to ensure adhesion of the subsequent layers to the surface. Next, a layer of lime-sand mortar is applied to even the surface, with care taken to avoid cracking. This layer is allowed to dry for up to a year.
- Once dry, a painting ground composed of white quartz sand, marble sand, marble meal, and infusorial earth is combined eight parts to one with slaked lime, and applied to the surface at a thickness of one eighth to one quarter inch. This layer is allowed to dry for several days, at which point a crust of carbonate will have formed on the surface. This crust is removed with a mixture of one part hydrofluosilicic acid to three parts distilled water, which is brushed on and allowed to dry for 24 hours, after which the surface is rinsed with distilled water.
- A hardening fluid of one part potassium silicate to two parts water is then brushed on and allowed to dry for 24 hours, before a second layer is applied and allowed to dry again. This surface may be painted immediately, or may sit unpainted for several years.
- The pigments to be used (selected from a set of thirty-eight) are treated with alkaline solutions of potash or ammonia to preempt any color change which might be caused by the alkaline fixative to come. Alternative pigments are suggested for those which cannot be used with an alkaline fixative.[2]
- Finally, the completed painting is fixed with an application of "waterglass" (sodium silicate) treated with ammonium carbonate, applied in a fine spray in several layers, until no more is absorbed. The chemical interaction of the fixative with the underlying pigments and ground create a material analogous to marble, and highly resistant to chemical corrosion.[3]
Keim's focus on the careful preparation of the painting ground was the result of his study of older frescos and their state of preservation.[5] Keim reportedly labored for twelve years to refine his process.[3]
References
- ↑ Rivington, J. A. (February 15, 1884). "A New Process for Producing Permanent Mural Paintings, Invented by Adolf Keim, of Munich". Journal of the Society of Arts. London: George Bell and Sons. 32 (1630): 245–257.
- 1 2 Jackson, F. Hamilton (1904). Mural Painting: Handbooks for the designer and craftsman. C. Scribner's Sons. ISBN 1112229248.
- 1 2 3 "A New Process of Mural Painting". The Builder. London: Henry Heathcote Statham. 46: 228. February 16, 1884.
- ↑ Spon, Edward; Spon, Francis N. (1886). Spons' Mechanics' Own Book: A Manual for Handicraftsmen and Amateurs (2nd ed.). London: E. & F.N. Spon. pp. 423–429.
- ↑ Osgood, J. R.; et. al. (1884). American Architect and Architecture. 15. p. 125.
This article is issued from Wikipedia - version of the 10/15/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.